>Teflon is a (fluorocarbon resin) or (flourine plastic) and has the same
>structure as polyethylene, in which the hydrogen is replaced by (flourine).
>OR a part may be replaced by (chlorine), in which case it is called a
>(fluorohalocarbon resin).
>
>Polymerized (tetrafluoro ethylene), aka PTFE, which carries the E.I. du Pont
>trade name of Teflon, formula (CF2*CF2)n is probably the most common
>solid form used for insulating materials, bearings, gaskets, insulating
>tapes, wire insulation, etc. This is a white waxy solid with specific
>gravity of up to 2.3, typical tensil strengths of up to 3500 psi, elongation
>of 250-350%, dielectric strength of 1000 v/mil and melting point of 594*F.
>
>Another commonly encountered material in electronic use and sometimes
>referred to generally as "Teflon", is Teflon FEP, which is a fluorinated
>(ethylene-propylene). In thin films (typically down to 0.0005"), it is most
>frequently found as insulation in capacitors. Typical tensil strength is
>3000 psi, elongation 250%, and dielectric strength 3200 V/mil.
>
>Neither PTFE or Teflon FEP emit phosgene upon decompositon at elevated
>temps.
>
>However, fluorothene plastic (which may be what Rich's info was referenced
>to) has the formula (CF2*CFCL)n and differ from (Teflon) in having one
>chlorine atom on every unit of the polymer chain, replacing the 4th
>fluorine atom. This is a (transparent) material with a specific gravity of
>~2.1, has tensil strengths of up to 9400 psi, but has a lower withstanding
>temp (as related to Teflon) of around 300*F. This material is sometimes
>called "Teflon" due to its similarity in chemical and polymer-structure
>make-up, and will emit phosgene upon decomposition at elevated temps.
>
thanks for the info, Dave
- Rich..., 805.386.3734, www.vcnet.com/measures.
--
FAQ on WWW: http://www.contesting.com/ampsfaq.html
Submissions: amps@contesting.com
Administrative requests: amps-REQUEST@contesting.com
Problems: owner-amps@contesting.com
Search: http://www.contesting.com/km9p/search.htm
|