[TowerTalk] Fwd: Fwd: N2JFS photos of bolts

Hans Hammarquist hanslg at aol.com
Thu Jan 9 16:10:03 EST 2014


It is very obvious that if we can keep moister out, no corrosion will take place, that's valid for almost all applications. The problem is that RTV application is not a long term solution. It may last 3, max 5 years. Reapplying RTV may, in some cases make bad thing worse as it may trap moister.

Regular maintenance by examine the bolts (hopefully in a short enough interval, be it 6 months or 15 years) is the only way. I plan is to replace them when I find it needed and assemble them with some type of seal. I, myself trust asphalt/tar more than RTV. Yes, it is sticky and messy but works. 

The bolts in the photo were about 25 years old and made of galvanized steel.

Hans - N2JFS

-----Original Message-----
From: Patrick Greenlee <patrick_g at windstream.net>
To: towertalk <towertalk at contesting.com>; Hans Hammarquist <hanslg at aol.com>
Sent: Thu, Jan 9, 2014 3:10 pm
Subject: Re: [TowerTalk] Fwd:  N2JFS photos of bolts

Thin oxidized coat protecting SS!!  Live and learn. Aluminum oxidizes on the 
surface and thereby protects the rest.

There is a type of corrosion for SS called oxygen deprivation corrosion but 
is usually of more interest in marine engineering/boats.

Once upon a time long long ago in a land far far away (San Diego California)... 
... might get him to apply 
silicone RTV (non acetic acid emitting type) to exclude moisture, a key 
ingredient in the electrolytic corrosion. and get things to last longer. 
Often these connections would not last one fishing trip when not properly 
protected from moisture.

Can we learn from this?  Maybe if we exclude moisture from the aluminum-SS 
contact we will not have an electrolyte and no electrolytic corrosion.

Patrick NJ5G

-----Original Message----- 
From: Hans Hammarquist
Sent: Thursday, January 09, 2014 12:30 PM
To: towertalk at contesting.com
Subject: [TowerTalk] Fwd: N2JFS photos of bolts

I was recommended but Universal to use galvanized bolts as the SS are not 
available in high enough grade. (I don't remember now what grade they 
recommended.) In my mind I will replace the bolts in a few (maybe 10 - 15) 
years. That will also give me an idea what condition they are.

I don't know how important the grade issue is and in my case I think I 
already have both "belt and suspenders" as I have a self-supporting tower 
equipped with guy wires. (The tower should be able to sustain 135 mph even 
if the base gives in.)

SS bolts are not a panacea. Even if the bolt doesn't corrode, which it 
actually might anyhow, it might damage the surrounding aluminum. Has 
something to do with Redox potential. The problem is that the Redox 
potential is not stable for aluminum and SS steel, in other word, you can 
not predict what will corrode when you connect and aluminum piece to a SS 
piece. When dirt cover the two metals it will form the destructive 
electrolyte, which will cause the corrosion. Depending on what the dirt 
contain you will get different results (place of corrosion). If you can keep 
the dirt away (not necessary easy) you can prevent or slow the corrosion 
rate (needless to say, really).

As a final note: SS needs access to air to stay stainless. A thin oxide 
layer on the steel surface serves as the corrosion prevention. If you cover 
the steel and the protective layer get damaged the corrosion can set in very 
fast (know that from experience, not from a tower, though).

Hans - N2JFS

-----Original Message-----
From: john <john at kk9a.com>
To: towertalk <towertalk at contesting.com>
Sent: Thu, Jan 9, 2014 9:28 am
Subject: Re: [TowerTalk] N2JFS photos of bolts

I had the same bolt issue with my first Universal tower. I have never seen
corrosion of the base, except in Aruba and it was only surface rust. I had
filled the square tube with concrete too keep if from filling with water.
As I recall the supplied bolts were just poor quality zinc plated.
Aluminum and galvanized steel touch in many areas of my tower systems with
no issues so I do not think it is a dissimilar metal problem. In fact, in
corrosive environments I have seem many instances were stainless steel
destroyed the aluminum it was in contact with so SS hardware has its

John KK9A - P40A

To: towertalk at contesting.com
Subject:[TowerTalk] N2JFS photos of bolts
From: kr2q at optimum.net
Date: Thu, 09 Jan 2014 12:31:15 +0000 (GMT)

Wow..those photos bring back lots of memories from the late 60's/early 

I had an aluminum (Heights) crankup tower (84 feet?).

I noticed some "rust" one year and pulled out the bolt that came with the
They looked well on the way to what you showed in your photos.

Yeah...you can't use steel bolts on an aluminum tower..this happens every

So I replaced all of the bolts with SS.  Worked great and let me sleep at

However, I was always worried about the Al to Steel junction at the base.
Also, the steel
triangles at the top/bottom of each (telescopic) section "rusted" 
metals - eaten
away) pretty badly.  I had SS triangles fabricated, but by the time they
arrived, I went off
to college and wen I returned, I found a greenhouse where my tower used to

So I bought some taper sections and no longer had a crank up.  My dad was
to let me "move the tower" to the other side of the house...again using SS
bolts..but still had
the same issue with the base.

When I got my own place, I bought steel crankup towers.  Heavier but no
about the
aluminum eating away the steel.

de Doug KR2Q